- The behaviour of Hydrogen Induced Cracking (HIC) was investigated into five kinds of material in NACE solution. 研究了五种材料在NACE溶液中的氢致开裂（HIC）行为。
- Abstract Corrosion resistance play an important role in the reliability of pipeline steels, and HIC (Hydrogen Induced Cracking) is one of failure forms for pipeline. 摘要 耐蚀性是影响管道可靠性的重要因素，其中氢致裂纹是管道的失效形式之一。
- The hydrogen induced cracking (HIC) of X70 pipeline steel was studied in H2SO4 solutions with different concentrations by means of electrochemical charging. 采用电化学充氢的方法研究了X70管线钢在不同浓度硫酸溶液中的氢致开裂(HIC)行为。
- The failure tube was analyzed. The results show that fracture was caused by hydrogen induced cracking initiated at brittle inclusion in the surface, though the sulphur content was only 0.003 wt %. 通过对开裂的渣油加氢冷高压分底排污水管线大小头的综合分析;结果表明在高硫化氢含量、高压力下;即使碳钢的含硫量达0.;003%25(质量分数);也可以由脆夹杂物引起氢致开裂
- According to analysis above mentioned, the failure potentiality of natural gas filter separator surely exists though no hydrogen induced cracking (HIC) had been found in the specimen. 根据以上分析结果，在对壳体材料的研究中虽然没有发现氢致裂纹等失效行为发生，但是仍然存在这种失效的潜在可能性。
- FRACTAL MODEL OF HYDROGEN INDUCED CRACKING 氢致裂纹扩展的分形模型
- Hydrogen Induced Cracking and Delayed Fracture 氢损伤和滞后断裂
- By chemical composition analysis,hardness test,metallographic examination and cracks analysis,the results indicate that the failure mechanism is hydrogen induced cracks (HIC). 通过化学成分分析、硬度测试、金相检验与裂纹分析,结果表明断裂失效机理为氢致开裂。
- FRACTAL STUDY DEVELOPMENTS OF HYDROGEN INDUCED CRACKING 氢致裂纹扩展的分形研究进展
- THE EFFECTS OF PLASTIC DEFORMATION ON HYDROGEN INDUCED CRACKING 塑性变形在氢致断裂中的作用
- THE EFFECT OF MICROSTRUCTURE ON HYDROGEN INDUCED CRACKING IN PIPELINE STEEL 管线用钢显微组织对氢致裂纹影响的研究
- Keywords Hydrogen induced crack Hydrogen concentration Overloading effects; 氢致开裂;氢浓度;过载效应;
- HAZ Structure,Toughness and Characteristics to Hydrogen Induced Cracking(HIC) of Steel 20MnNiMo 20MnNiMo钢焊接热影响区的组织和韧性及其氢致裂纹特征
- Keywords Fracture;Mechanism;Hydrogen induced cracking （HIC）;Anodic dissolution;Steel;Hydrochloric acid;Ferric ion; 脆断;机理;氢致开裂;阳极溶解;钢;盐酸;铁离子;
- Keywords tyre steel;macrostructure;casting temperature;hydrogen induced cracking;flaking; 轮箍钢;低倍组织;连铸温度;氢致开裂;白点;
- the sulfide stress corrosion cracking (SCO developed on the high-strength steel of pressure vessels and hydrogen induced cracking (HIC or SOHIC). 通过喷钙处理改变夹杂物形状和提高钢材纯净度是目前抗氢诱导裂纹常用的两种方法。
- Keywords X70;Pipeline steel;Welding joint;acicular-ferrite;Hydrogen Induced Cracking （ HIC ）;banded microstructure;non-metallic inclusion; 管线钢;焊接接头;针状铁素体;氢诱发裂纹（HIC）;带状组织;非金属夹杂;
- Keywords Diffusible hydrogen Absolute humidity Hydrogen induced crack Welding process; 扩散氢;湿度;氢致裂纹;焊接工艺;
- Keywords SPV50Q steel;LPG spherical tank;Stress orientation hydrogen induced crack （SO-HIC）;Repair technology; SPV50Q钢;液化气球罐;应力诱导型氢致裂纹;修复技术;
- Keywords Pipeline Steel Hydrogen Induced Crack （HIC） Characteristic Measurement; 管线钢管;氢致裂纹;特点;措施;