By chemical composition analysis,hardness test,metallographic examination and cracks analysis,the results indicate that the failure mechanism is hydrogen induced cracks (HIC).

• 通过化学成分分析、硬度测试、金相检验与裂纹分析,结果表明断裂失效机理为氢致开裂。