- Electro-chemical Detachment Process of Through-hole Porous Anodic Alumina Membrane 通孔氧化铝模板的强脉冲电化学剥离研究
- porous anodic alumina membrane 氧化铝膜
- Keywords porous anodic alumina membranes;anodic oxidization;nanostructure; 多孔氧化铝模板;阳极氧化法;纳米结构;
- Porous anodic alumina membranes 多孔铝阳极氧化膜
- The influence of annealing, degreasing, electropolishing on the morphology of porous anodic alumina was investigated. 对铝的预处理工艺进行了研究，详细探讨了高温退火、除油及电化学抛光等对多孔阳极氧化铝形貌的影响。
- The influence of annealing,degreasing,electropolishing on the morphology of porous anodic alumina was investigated. 对铝的预处理工艺进行了研究,详细探讨了高温退火、除油及电化学抛光等对多孔阳极氧化铝形貌的影响。
- A new type of agent for stripping aluminum from porous anodic alumina films has been developed by the method of the orthogonal experiment. 采用正交实验方法,研制出了一种新型多孔阳极氧化铝模板剥铝剂。
- The result shows that the anodic alumina membranes produced in oxalic acid or phosphoric acid electrolyte are porous double-layer films. 在硫酸电解液中形成的直流阳极氧化铝膜的等效电路中无多孔层信息。
- Highly ordered iron oxide nanowire arrays were prepared by sol-gel tem plate method within the pores of anodic alumina membrane (AAM). 氧化铁纳米线阵列的制备未见报导,因此氧化铁纳米线阵列的制备及其性质的研究具有重要的意义。
- Experiments indicate that acetone exhibits the best degreasing effect and that well-arranged porous anodic alumina film is obtained without annealing and electropolishing. 实验结果表明，采用丙酮除油效果最好，不经高温退火和电化学抛光仍能得到高度有序的多孔阳极氧化铝膜，使制备工艺得到了简化。
- We report the numerical calculation results of ordered silver nanowire arrays embedded in anodic alumina membrane (AAM). 摘要报道了组装在氧化铝模板中的银纳米线有序阵列光偏振的数值计算结果。
- After immersed in Cr2(SO4)3 solution followed by calcining at different temperatures, Cr3+ doped porous anodic alumina (PAA:Cr) were prepared with different crystal structure. 以氧化铝模板(PAA)为母体;通过浸泡Cr2(SO4)3溶液掺入三价Cr离子;将掺杂的PAA煅烧使其晶化;不同的煅烧温度形成不同的相.
- The method of producing anodic alumina membrane is presented.The route to synthesize nanowires through electrodeposition with it as a membrane is reviewed. 本文论述了阳极氧化铝模板的制备方法和以其为模板利用电沉积技术制备纳米线的合成路线。
- The preparation of porous anodic alumina film is simplified because of the two-step anodic oxidation method that eliminates the influence of disfigurement inside and on the surface of aluminium. 其原因是两步阳极氧化法可以消除铝的内部结构及表面缺陷对多孔氧化铝膜有序性的影响。
- A review was given of porous anodic alumina films(PAAF)formation on aluminum by two-step anodization method in acid electrolytes at constant voltage. 直流恒压下,在酸性溶液中对铝实施两步阳极氧化制备了多孔氧化铝膜。
- Porous anodic alumina (PAA) formed in acid solution by anodizing of metal aluminum has porous structure with ordered nanopore arrays. 金属铝在酸性溶液中阳极氧化得到的多孔性氧化铝薄膜具有有序排布的纳米量级的孔阵列。
- This article introduces the fabrication of the porous anodic alumina films which have ordeed pore arrangement by using a two-step anodization process. 文章介绍采用二次阳极氧化法制备孔洞规则、有序的多孔氧化铝膜的工艺。
- Porous anodic alumina(AAO) films have been prepared by electrochemically anodizing aluminium in sulfuric acid、oxalic acid and phosphoric acid solutions,respectively. 采用电化学方法分别在硫酸、草酸、磷酸电解液中制备了多孔阳极氧化铝(AAO)薄膜.
- The equivalent circuit models corresponding to these anodic alumina membranes were established. 结果表明:在草酸、磷酸电解液中形成的阳极氧化铝膜是多孔双层膜。
- Abstract This article introduces the fabrication of the porous anodic alumina films which have ordeed pore arrangement by using a two-step anodization process. 摘要 文章介绍采用二次阳极氧化法制备孔洞规则、有序的多孔氧化铝膜的工艺。