您要查找的是不是：
- Special Shaped Catalysts for Reaction in Fixed Bed Reactor with Molten Salt Bath 异形催化剂在熔盐浴固定床反应器内反应的研究
- molten salt bath 熔融盐槽
- Salt Bath Started by Salt Slag Re. 盐渣电阻启动电极盐浴炉。
- Salt Bath Started by Salt Slag Resistor. 盐渣电阻启动电极盐浴炉盐渣电阻启动电极盐浴炉。
- The results has shown that Sn was deposited from SnCl 2 BPC molten salt. 结果表明 ,SnCl2 BPC熔盐可用于Sn的电镀 ;
- Spectroscopic Investigation of New Binary Molten Salt Electrolytes Based on Li ClO_4 with Acetamide? 高氯酸锂-乙酰胺新型二元熔盐电解质的谱学研究
- It was investigated that chromizing in borax salt bath and melting hydrochloride. 研究了硼砂盐浴渗铬和氯系熔盐渗铬。
- Meanwhile, different thermodynamic models for the prediction of new molten salt hydrates have been evaluated. 介绍了预测熔盐水化物相图的各种热力学模型及其优缺点;
- The structure of electrode neutral salt bath titanized layer of T12 steel has been studied by means of microscope, EPMA,X-ray diffractometer and TEM. 用光学显徽镜、电子探针、X射线衍射仪和透时电镜研究了T12钢电极中性盐浴渗钛层的组织结构。
- In this paper,aluminum-scandium alloys were prepared starting form scandium oxide by molten salt electrolysis. 本文采用了熔盐电解法研究铝钪合金的制备。
- The result shows that the porosity of nitrided layer is due to the over concentration of CNO- in the salt bath. 试验结果表明，渗层疏松主要是由于盐浴内CNO－浓度过高所致；
- Protecting effect of SQA coating was compared with that of commercial paints or salt bath treatment. 用SQA型涂料和商品涂料进行加热保护及用盐浴处理,对保护效果进行了比较,结果表明SQA型是一种较为理想的高、中温防氧化脱碳涂料。
- Electrodeposition of Sn from SnCl 2 1 butylpyridinium chloride (BPC) ambient temperature molten salt electrolytes was studied. 在测定了室温型SnCl2 BPC熔盐的物理、电化学性质的基础上 ,进行了镀锡的研究。
- The carbon steel used in the mixed salt bath which is the mixture of broax and neutral salt for vanadinizing. 采用硼砂与中性盐混合盐浴对碳钢试样进行渗钒,研究钢含碳量及保温时间对覆层厚度的影响。
- As a new kind of methods to prepare inorganic material powders. molten salt method (MSM) and some of its applications are recommended in this paper. 摘要介绍了一种新的无机材料粉体的制备方法熔盐法，以及该方法的部分应用。
- If one takes a salt bath and requires salt, salt will be absorbed through the pores into the crystalline form. 如果你做了一次盐浴且身体正需要盐，那么盐就将透过毛孔而被吸入到水晶形体中。
- The advantages of u sing heat carries for indirect heating were shown as early as using water,vapor, molten salt and liquid metal. 利用载体间接加热的优越性，早在利用水、蒸汽、熔盐和液态金属的初期就已经显现出来了。
- Immediate quenching and tempering process of steel T10 after low temperature salt bath chromizing was studied. 研究了 T10钢在低温盐浴渗铬后直接淬火并回火工艺。
- The technology of recovering certified molten salt and RE oxide from scrapped molten salt in fluoride electrolysis has been studied in this paper. 主要研究了从氟化体系熔盐电解过程产生的废熔盐回收合格熔盐和氧化稀土的工艺条件;
- The austempering in salt bath can increase the impact toughness and wear resistance of the high alloy white cast iron. 盐浴等温淬火可提高高合金白口铸铁的冲击韧性及耐磨损性能。