您要查找的是不是：
- hot dip galvanised process 热浸镀锌法
- hot dip galvanised 热浸镀锌
- A hot dip Zn 5%Al RE coating on high carbon steel wire is tested. 试验了在高碳钢丝表面上热浸镀Zn 5%25Al RE合金层。
- With carbon steel pretreated with flux, hot dip coating process and bimetal producing of ZAS35 alloy/carbon steel as well as bimetal interface characteristic were studied. 研究了经熔剂法预处理的碳钢热浸镀ZAS35锌合金工艺、ZAS35锌合金 /碳钢双金属制作工艺及双金属界面特性。
- XIA Yuan,YAO Mci,LI Tie-fan.Coating formation process and microstructure during hot dip aluminizing (HDA) on steel[J].The Chinese Journal of Nonferrous Metals,1997,7(4):154-158. [4]夏原;姚枚;李铁藩.;热浸铝镀层的微观结构及形成机理[J]
- The Annealing Furnace is a key Equipment for any Hot Dip Galvanizing Line. 对于任何连续热镀锌线退火炉都是关键设备。
- High structure strengh,hot dip galvanized,greatly protract time of use. 高强度管材、产品经热镀锌处理、大大地延长了使用寿命；
- Surface quality of hot dip plating Zn-Al alloy were further improved. 采用该合金助镀剂进行Zn Al合金热浸镀的样品 ,表面质量得到进一步改善。
- Experiment results showed that the process of Hot Dip Aluminum and complex Boronisation on the A3 surface is feasible, it had a continuous layer between diffusion layer and matrix and a better hardness gradient. 试验表明 :A3钢表面浸镀扩散渗铝复合渗硼工艺可行 ,渗层与基体形成了连续的扩散层 ,并且具有良好的硬度梯度。
- XIA Yuan, YAO Mei, LI Tie-fan.Coating formation process and microstructure during hot dip aluminizing(HDA) on steel [J].The Chinese Journal of Nonferrous Metals, 1997, 7 (4): 154-158. [4]夏原; 姚枚; 李铁藩.;热浸铝镀层的微观组织结构及形成机理[J]
- The cold rolled coils entered into hot dip galvanizing workshop are put on waiting position and then transferred to uncoiler by coil car. 冷轧卷进入热镀锌车间后置于待处理位置,然后通过上卷小车送至开卷机。
- Commodity:Hot dipped galvanized steel in coil . 货物名称:冷轧热镀锌卷。
- The effects of aluminum bath temperature, immersion time and silicon content on hot dip aluminum for HT200 are studied. 研究了热浸温度、时间及硅含量对HT200热浸渗铝的影响。
- The technique of hot dip Zn-Ni alloy coating is an effective method for solving the reactive steel problem in hot dip galvanizing. 热浸锌镍合金镀层技术是解决活性钢热镀锌问题的有效方法。
- Effects of cooling rate on eutectic microstructure of Zn-(0.24Ni) alloy for hot dip galvanization were investigated. 研究了冷却速度对用于热浸镀Zn的Zn0.;24Ni合金共晶组织的影响。
- The effect of Ni content in Zn bath on thickness of hot dip galvanized coating was studied using SEM. 应用SEM、EPMA等方法研究了锌浴中镍含量对热浸锌镀层厚度的影响，试验结果表明：当锌浴中镍含量小于0.;12%25 (wt)时，镀层随镍含量增加而减薄；
- The tensile properties and corrosion resistance of hot dip 55%Al Zn alloy coating steel are investigated. 研究了热浸镀 5 5%25Al Zn合金镀层钢的室温拉伸性能和耐蚀性能。
- Drilling method of pin hole: the pin hole shall be predrilled by supplier prior to hot dip galvanization. 销钉孔的钻法：销钉孔应为供应商在热镀锌预钻好。
- Bitumen coated and Hot Dip Galv. steel fence post. the length range from 450mm to 2400mm.... 发布者：马传圆所在地：新疆吐鲁番地区行业：五金、工具职位：外销员工作年限：在读学生
- Technologies were then developed including using of zinc alloy, such as Zn-Mn, Zn-Mg and Zn-Ni alloy baths, and high temperature hot dipping process. 为此，国外发展了多种热镀锌技术，包括在锌浴中添加合金元素的多元合金、锌锰合金、锌镁合金和锌镍合金热镀锌技术及高温镀锌技术。