- The passivating process and formulation of bath solution for zinc hot dipped coating with higher alloy content were investigated and discussed. 研究了合金含量较高的热浸镀锌层的钝化工艺及配方，探讨了钝化液组分对钝化膜性能的影响及钝化原理，检测了所研制钝化膜的性能。
- The recommended passivating solution could be used not only for passivating zinc hot dipped coating but also for Zn-Ni and Zn-Fe alloy coating. 结果表明，该钝化液适合于热浸锌合金镀层的表面钝化处理，亦适用于电镀锌及锌合金镀层、锌合金压铸件等的钝化处理，应用范围宽，且工序简化，抛光和钝化一步完成。
- Progress in Zinc Hot Dipping of Reactive Steel 国外活性钢热镀锌技术研究的进展
- Zinc hot dip 热镀Zn
- The key to realize internal heating in hot dip galvanizing is materials with good corrosion resistance to molten zinc. 实现热镀锌内加热技术的关键是解决耐锌蚀材料的问题。
- For acquiring new alloy coating with good corrosion resistance and production cost equivalence with hot dip zinc coating,the hot-dip Zn-Mg alloy coating of containing 0. 质量分数,下同)的热镀锌镁合金镀层,对各种成分的锌镁合金镀层进行了电化学测试和中性盐雾实验,并通过电子扫描显微镜观察了镀层的表面形貌。
- A hot dip Zn 5%Al RE coating on high carbon steel wire is tested. 试验了在高碳钢丝表面上热浸镀Zn 5%25Al RE合金层。
- In this paper, the adhesiveness and the corrosion resistance of hot dip Zn 0.1Ni alloy coating are studied by the bending test and the salt spray test and are compared with those of hot dip zinc coating. 通过弯曲试验和盐雾试验，研究了热浸Zn?0.;1Ni合金镀层的粘附性能和耐腐蚀性能，并与热浸锌镀层对比。
- The Annealing Furnace is a key Equipment for any Hot Dip Galvanizing Line. 对于任何连续热镀锌线退火炉都是关键设备。
- In this paper, the development of the equipment for new type continuous hot dip galvanizing lines including welding machine, cleaning equipment, continuous annealing furnace, zinc pot, galvannea. 在此简要介绍了新型带钢连续热镀锌机组设备(包括焊机、清洗设备、连续退火炉、锌锅设备、合金化炉及平整机等)的发展情况。
- High structure strengh,hot dip galvanized,greatly protract time of use. 高强度管材、产品经热镀锌处理、大大地延长了使用寿命；
- Surface quality of hot dip plating Zn-Al alloy were further improved. 采用该合金助镀剂进行Zn Al合金热浸镀的样品 ,表面质量得到进一步改善。
- The cold rolled coils entered into hot dip galvanizing workshop are put on waiting position and then transferred to uncoiler by coil car. 冷轧卷进入热镀锌车间后置于待处理位置,然后通过上卷小车送至开卷机。
- The effects of aluminum bath temperature, immersion time and silicon content on hot dip aluminum for HT200 are studied. 研究了热浸温度、时间及硅含量对HT200热浸渗铝的影响。
- Commodity:Hot dipped galvanized steel in coil . 货物名称:冷轧热镀锌卷。
- Effects of Rare Earth on Hot Dip Zinc Alloys 稀土在锌基热镀合金中的作用研究
- no zinc flower hot dip galvanized sheet 无锌花镀锌板
- The technique of hot dip Zn-Ni alloy coating is an effective method for solving the reactive steel problem in hot dip galvanizing. 热浸锌镍合金镀层技术是解决活性钢热镀锌问题的有效方法。
- Technologies were then developed including using of zinc alloy, such as Zn-Mn, Zn-Mg and Zn-Ni alloy baths, and high temperature hot dipping process. 为此，国外发展了多种热镀锌技术，包括在锌浴中添加合金元素的多元合金、锌锰合金、锌镁合金和锌镍合金热镀锌技术及高温镀锌技术。
- Effects of cooling rate on eutectic microstructure of Zn-(0.24Ni) alloy for hot dip galvanization were investigated. 研究了冷却速度对用于热浸镀Zn的Zn0.;24Ni合金共晶组织的影响。