The results show that the main causes are severe welding defect,material quality and the cracks formed at elevated temperature, high pressure and corrosion conditions.

• 研究表明，早期失效的主要原因是严重的焊接缺陷及材质问题，以及受高温、应力、腐蚀等因素影响而形成的裂纹。