- The copolymer latex of butyl acrylate and VAE was prepared by interpenetrating polymer networks (IPN) method. 以互穿聚合物网络(IPN)方法合成丙烯酸丁酯与VAE共聚物乳液。
- Butyl acrylate(BA) was grafted polymerized onto starch by using ceric ammonium nitrate as initiator in aqueous medium. 以硝酸铈铵为引发剂,以未经精制处理的丙烯酸丁酯为接枝单体,在水相介质中制备了玉米淀粉接枝丙烯酸丁酯;
- Vinyl acetate and butyl acrylate as mixed monomer can be used to prepare high solid content water based white emulsion. 以醋酸乙烯及丙烯酸丁酯为混合单体来制备高固含量水基白乳胶。
- A polystyrene(PS)/poly(butyl acrylate)(PBA)composite emulsion was produced by seed emulsion polymerization of styrene . 聚苯乙烯(PS)和聚丙烯酸丁酯(PBA)复合乳液是无皂乳液聚合反应生成的,采用丙烯酸丁酯加到聚苯乙烯种子微粒中反应得到的。
- The poly(methyl methacryate)macromer was copolymerized with butyl acrylate i n benzene to form the graft copolymer. 研究了聚甲基丙烯酸甲酯大单体与丙烯酸丁酯在苯中的共聚。
- Butyl acrylate ( BA) was grafted polymerized onto starch by using ammonium ceric nitrate a initiator in aqueous medium. 以硝酸铈铵为引发剂,以未经精制处理的丙烯酸丁酯为接枝单体,在水相介质中制备了丙烯酸丁酯接枝玉米淀粉。
- Good results have been obtained for both polyether urethane and nitrate esters when using 2,6 di t butyl 4 methyl phenol(BHT) as stabilizer. 2 ,6-二叔丁基 - 4 -甲基酚 (BHT)对硝酸酯和聚氨酯粘结剂均具有良好的稳定作用。
- The pigment printing binder of textile for environmental protection was prepared by copolymerization with butyl acrylate, methyl methacrylate and styreneis as the main materials. 摘要以苯乙烯、甲基丙烯酸甲酯和丙烯酸丁酯为主要原料，经乳液聚合，制成了环保型的涂料印花粘合剂。
- The graft copolymerization of butyl acrylate(BA)onto chloroprene rubber(CR) is carried out in methylbenzene-ethyl acetate solvent by using a new type of efficient initiator. 以一种新型的高效引发剂,在甲苯-乙酸乙酯混合溶剂中进行氯丁橡胶(CR)与丙烯酸丁酯(BA)的接枝共聚反应。
- A hindered polyetherketone endcapped with p (t butyl)phenol was synthesized. 1H NMR technique was used to seek for the number average molecular weight of this new polymer. 以对叔丁基苯酚为封端剂，合成带烷端基的多苯基取代联苯型聚醚酮，测定其1H－NMR谱，根据链中芳环质子共振峰与链端基质子峰积分强度比求解分子量。
- The pyrolyzed behavior of tetrabasic copolymer (2-butene,methyl methacrylate, butyl acrylate, octyl acrylate) at various temperature was investigated. 报道了2丁烯、甲基丙烯酸甲酯、丙烯酸丁酯、丙烯酸辛酯四元共聚物在不同裂解温度下的热裂解行为。
- This paper presents the preparation of the graft copolymer alloy of pullulan with butyl acrylate using manganic pyrophosphate as initiator. 研究在水介中焦磷酸锰引发下,普鲁兰/聚丙烯丁酯接枝物合金的制备、组成的控制及接枝共聚反应速率。
- The particle-design method was used in this paper to prepare PAE modified by Poly (butyl acrylate) -core/ PMMA-shell Latex. 运用粒子设计的方法制备了PAE改性的聚丙烯酸丁酯／甲基丙烯酸甲酯核壳乳液。
- A study of the grafted copolymerization of potato starch with butyl acrylate as comonomer,and APS as initiator by microwave radiation has been mode. 研究在微波场中用APS引发土豆淀粉与丙烯酸丁酯的接枝共聚规律。
- The effects of ethyl acrylate, butyl acrylate and the kinds of POF coating technology, on loss and flexility, were discussed. 探讨了丙烯酸乙酯、丙烯酸丁酯对聚合物光纤损耗、柔韧性等性能的影响，以及各种涂覆工艺对聚合物光纤损耗的影响。
- The thickening agent of emulsion is made from methacrylic acid and butyl acrylate and uses with 760 adhesive in fabric printing. 进行了甲基丙烯酸和丙烯酸丁酯为组份的乳液增稠剂的合成实验,并同760粘合剂配套使用,用于涂料印花。
- In the second path, the regiospecific reaction characteristic of the chlorination of salicylic acid by t butyl hypochlorite was used.When t butyl hypochlorite is used as chloride in t... 次氯酸叔丁酯对水杨酸的氯代有很强的区域专一性反应特性,用其作为氯代剂合成硝苯柳胺收率为81%25,产品纯度979%25;
- A study of the grafted copolymerization of potato starch with butyl acrylate as comonomer, and APS as initiator by microwave radiation has been mode. 摘要研究在微波场中用APS引发土豆淀粉与丙烯酸丁酯的接枝共聚规律。
- The influence facts upon adhesive strength,such as hardening agent content, n butyl acrylate content,synthesis condition were discussed. 考察了固化剂含量、预固化及预聚合时间、丙烯酸丁酯含量以及引发剂含量对胶粘剂力学强度的影响。
- High performance quadripolymer latex for waterborne anti-corrosive paint is synthesized by use of butyl acrylate,styrene,acrylonitrile and acrylate acid. 用丙烯酸丁酯、苯乙烯、丙烯腈、丙烯酸共聚,得到性能优良的水性防腐涂料乳液;