- The forming mechanism of the submerged nozzle clogging is investigated. 研究了浸入式水口堵塞的形成机理。
- Submerged nozzle must be preheated before casting.Now,burning the coal gas is the usual preheating method. 浸入式水口在浇钢以前必须进行充分预热,利用燃烧的煤气烘烤水口是常用的预热烘烤方式。
- The clogging was mainly due to the attachment of oxide particles onto the inner surface of the submerged nozzle followed by sintering. 堵塞沉积主要是由于氧化物颗粒附着到浸入式水口耐火材料的内表面，继而烧结在一起所致。
- The thermal shock stability, cleanness of molten steel and suitable protective slag function for fused quartzose and aluminious carbon submerged nozzle are analyzed and compared. 对熔融石英质和铝碳质浸入式水口热震稳定性、洁净钢水、适用保护渣性能进行分析对比,并对影响其使用寿命、堵塞原因及其工艺效果作进一步的阐述。
- The main reason that the submerged nozzle clogged during continuous casting of high aluminum low carbon steel is aluminate that aggraded the submerged nozzle wall. 中薄板坯连铸机生产低碳高铝钢过程中,浸入式水口堵塞的主要原因是水口与钢水之间产生化学作用和钢水中的氧化铝夹杂物在水口壁上沉积。
- Al2O3 adhesion on the innerface of submerged nozzles decreases the productivity greatly in continuous casting process of steel-making industry. 连铸工艺中Al2O3在浸入式水口内壁附着造成的堵塞严重影响了生产效率，开发防止Al2O3附着的新材料成为解决这一问题的主要方向。
- Technological Optimization of Slag Line Alter on Submerged Nozzle 浸入式水口变渣线的工艺优化
- Clogging mechanism and improvement measures of submerged nozzle 浸入式水口堵塞的机理及其改善措施
- DEVELOPMENT AND APPLICATION OF SUBMERGED NOZZLE ONLINE ROASTER 浸入式水口在线烘烤器的开发与应用
- STUDY ON STRUCTURE TYPE OF SUBMERGED NOZZLE FOR CONTINUOUS CASTING BILLET MOLD 方坯连铸结晶器浸入式水口结构类型的研究
- Study of preheating temperature field of submerged nozzle in burning method 浸入式水口燃烧式烘烤预热温度场研究
- Property and application of submerged nozzle for thin slab continuous casting 薄板坯连铸用浸入式水口的性能与使用
- Numerical simulation of submerged nozzle for thin-slab continuous casting 薄板坯连铸浸入式水口结构数值模拟
- Inspecting on the sample from the rod during piling accident,it is showed that the rod piling are origned from the fracture of the broken submerging nozzle wrapped in liquid steel. 通过对堆钢盘条样品的检验分析,表明造成盘条堆钢的原因是连铸过程中的水口断裂进入钢液形成的夹杂造成的。
- Abstract Inspecting on the sample from the rod during piling accident, it is showed that the rod piling are origned from the fracture of the broken submerging nozzle wrapped in liquid steel. 摘要 通过对堆钢盘条样品的检验分析，表明造成盘条堆钢的原因是连铸过程中的水口断裂进入钢液形成的夹杂造成的。
- Inspecting on the sample from the rod during piling accident, it is showed that the rod piling are origned from the fracture of the broken submerging nozzle wrapped in liquid steel. 摘要通过对堆钢盘条样品的检验分析，表明造成盘条堆钢的原因是连铸过程中的水口断裂进入钢液形成的夹杂造成的。
- She longed to clout him in the nozzle. 她真想猛揍一下他的鼻子。
- The submarine submerged to avoid enemy ships. 该潜艇潜入水下以躲避敌舰。
- Our ship was able to haul up just before it hit the submerged reef. 我们的船就在要撞上暗礁的时候停住了。
- Influence of Submerged Nozzle on Temperature and Flow Fields in Molten Pool During Twin-Roll Strip Casting 双锟铸轧过程中水口对熔池内温度场和流场的影响