- The porous alumina film prepared by anodization of aluminum in chromic acid under constant voltage and direct current can absorb infared wave. 在铬酸中采用直流恒压铝阳极氧化法制备氧化铝多孔膜，经测试这种多孔膜具有红外吸波性能。
- By measuring Current j-t curves were studied formational process of porous alumina films. 在直流恒电压条件下,以草酸为电解液制备了多孔氧化铝模板。
- Porous alumina films with nanometer size have been fabricated through electrochemical method in the aqueous solutions of sulfuric acid and oxalic acid. 采用电化学方法在硫酸和草酸溶液中制备了具有纳米结构的多孔氧化铝。
- Transversely Isotropic Elasticity of Porous Alumina Film 多孔氧化铝薄膜横观各向同性弹性性质的研究
- The appearance of the aluminium foil before and after annealing was observed with a metallographic microscope,and the surface morphology of porous alumina films was examined using SEM. 用金相显微镜观察了铝箔退火前后的表面形貌,并结合扫描电镜对多孔氧化铝薄膜进行了形貌观察和表征。
- Research Progress of Preparation of Porous Alumina Film and Its Application 氧化铝多孔膜的制备及其应用研究新进展
- Studies on Formation of Anodic Porous Alumina Film and its Infrared Wave Absorbing Properties 酸性溶液中铝阳极氧化多孔膜的形成及其红外吸波特性研究
- Study of CdS Nanowires Deposited in Silicon Based Porous Alumina Film by Non-aqueous Electrochemical Deposition 硅基多孔氧化铝模板非水电沉积CdS纳米线的研究
- EFFECT OF PHOSPHORIC ACID CONCENTRATION ON FORMATION OF BARRIER LAYER OF ANODIC POROUS ALUMINA FILM 磷酸浓度对铝阳极氧化多孔膜阻挡层形成过程的影响
- Keywords porous Alumina film;uniaxial tensile tests;ESPI;homogenization theory;nanoindentation;finite element; 多孔氧化铝薄膜;单轴拉伸;电子散斑干涉;均匀化理论;纳米压痕;有限元;
- Study of Nanostructures and Reflective Spectra of Porous Alumina Films 多孔氧化铝薄膜的纳米结构和光谱特性研究
- porous alumina film 多孔氧化铝膜
- Study of the structure of the porous alumina filme and the property of infrared wave-absorption 铝多孔氧化膜的结构及红外吸收特性
- Experiments indicate that acetone exhibits the best degreasing effect and that well-arranged porous anodic alumina film is obtained without annealing and electropolishing. 实验结果表明，采用丙酮除油效果最好，不经高温退火和电化学抛光仍能得到高度有序的多孔阳极氧化铝膜，使制备工艺得到了简化。
- The preparation of porous anodic alumina film is simplified because of the two-step anodic oxidation method that eliminates the influence of disfigurement inside and on the surface of aluminium. 其原因是两步阳极氧化法可以消除铝的内部结构及表面缺陷对多孔氧化铝膜有序性的影响。
- Tests show Fe was deposited in porous alumina only in ferrous solution with JF,and the color of the oxide film darkens gradually with the Fe-content in the oxide film,but their relation is not a simple linear rule and the real black can not be gained. 试验结果表明只有在含有JF的亚铁盐溶液中才能在氧化膜中沉积铁,膜的颜色随氧化膜中铁的含量增加而加深,但不成正比关系,真黑色的膜难以得到。
- Porous alumina templates were obtained by one and two-step anodization respectively. 分别采用一次阳极氧化和二次阳极氧化制备了多孔氧化铝模板。
- Porous alumina membrane is prepared by aluminum anodizing in given acidic solution. 直流恒压下,在酸性溶液中对铝实施两步阳极氧化制备了多孔氧化铝膜。
- porous alumina films Al2O3多孔膜模板
- A review was given of porous anodic alumina films(PAAF)formation on aluminum by two-step anodization method in acid electrolytes at constant voltage. 直流恒压下,在酸性溶液中对铝实施两步阳极氧化制备了多孔氧化铝膜。