您要查找的是不是：
- Study on erosion resistant nano epoxy adhesive coating 环氧胶粘纳米涂层冲蚀磨损性能研究
- Under the high-speed work condition, the brittleness of epoxy adhesive coating leads to its bad slurry erosion performance. 但由于环氧树脂胶粘层脆性大，在较高速度的浆体冲蚀工况下，其抗浆体冲蚀磨损性能并不理想。
- According to the analysis of wearing curve by tests and wear topography by SEM, slurry erosion wear mechanism of modified epoxy adhesive coating was discussed. 浆体冲蚀磨损机制的分析讨论是结合磨损试验获得各种情况下的磨损曲线与扫描电镜观察到的磨损形貌进行分析的。
- In this experiment nano- and macro-filler were added into epoxy adhesive to increase the relative abrasion resistance (RAR) of epoxy coating and function of the filler effecting on epoxy adhesive coating . 为了提高环氧粘涂层的耐磨性,本试验通过在环氧胶粘剂中加入纳、微米填料,研究了纳微米填料对环氧胶粘剂涂层耐磨性的影响规律。
- Influence of NANO-MMT on the property of epoxy adhesive coating 纳米蒙脱土对环氧树脂胶黏涂层性能的影响
- Study on erosion wear properties of epoxy adhesive coating 环氧胶粘涂层冲蚀磨损特性研究
- Effect of Filler and Curing Procedure on Hardness of Epoxy Adhesive Coating 固化工艺对环氧胶粘涂层硬度的影响
- The Effect of Filler on Characteristic of the Epoxy Adhesive Coating 碳化硼对环氧胶粘涂层机械性能的影响
- Effect of Filler and Curing Procedure on the Hardness of Epoxy Adhesive Coating Layer 固化条件对环氧玻璃鳞片涂层界面强度的影响
- Effects of Filler and Curing Parameters on the Hardness of Epoxy Adhesive Coating 填料与固化工艺对环氧胶粘涂层硬度的影响
- nano- epoxy adhesive coating 纳米环氧树脂胶粘涂层
- New product of epoxy resin,curing agent,addtive and developing progress in epoxy adhesive,coating and comosite for airliner were introduced. 介绍了环氧树脂、固化剂及助剂方面的新产品以及新型环氧树脂胶粘剂、涂料、大飞机用复合材料等的开发进展。
- Familiar with epoxy adhesive products and market, has related sales experience. 熟悉环氧类胶粘剂产品及市场,具备行业销售经验。
- Epoxy adhesive in stick form for repairing broken items or patching leaks. 用于修补容器，管道等的破损；
- A soft, adhesive coating material, such as plaster, grease, or mud. 涂料柔软粘稠的涂抹原料，如泥灰、润滑脂或泥浆
- The specimens were made from two glass arms joined with a 0.005-in. layer of epoxy adhesive. 制作的试样是把两块玻璃臂用0.;005时厚环氧粘合剂涂层胶合成的。
- When being filled with composite of nano- and macro-filler the RAR of coating was as 2.57 times as that of 45 steel and 2.85 times higher than that of the pure epoxy adhesive coating. Which was also higher than that of coating with nano-filler. 加入纳微米复合填料其相对耐磨性为正火态45钢的2.;57倍;和纯环氧胶粘剂涂层相比;提高幅度可达2
- All the robs are glued together by instant glue first and then by epoxy adhesive. 所有失去了粘在一起，是透过即时胶水第一，然后由环氧胶粘剂。
- The reason for reduction of bonding performance of epoxy bonded joint was the degradation of epoxy adhesive. 胶粘剂分子链的降解是环氧胶接接头胶接性能降低的主要原因；
- However, when dicyandiamide and imidazole were added together in epoxy adhesive, the amount of dicyandiamide decreased to 15%. 而复合使用改性双氮胺和咪唑，在保证性能和固化时间的前提下，双氰胺的用量可减少至15%25。