- Microporous polypropylene hollow fiber membranes were prepared by the melt spinning and cold-drawing method. 通过熔纺/冷拉伸法制备了微孔聚丙烯中空纤维膜。
- Polypropylene granulate add master batch of disperse dyes as raw to make dyed mo dified polypropylene fiber by polyblending melt spinning method. 以聚丙烯切片及添加分散染料的可染母粒为原料,采用共混熔融纺丝方法制备染色改性丙纶。
- Application of non polyurethane,polyester polyurethane,polyether polyurethane and chain extender on the melt spinning of elastic fiber is introduced . 介绍了非聚氨酯类、聚酯型聚氨酯类、聚醚型聚氨酯类聚合物及扩链剂在熔纺弹性纤维上的应用。
- The molecular sieve modified PET fiber was prepared by blending and melt spinning PET chip with molecular sieve and additives,like dispersant,cross linker,at different ratios. 将分子筛、添加剂(分散剂、交联剂)以不同的比例和PET切片共混进行母粒法熔融纺丝,制得分子筛改性PET纤维,并测定纤维的力学性能、吸湿性能和染色性能。
- A kind of high strength and high modulus fiber was prepared by melt spinning and drawing of high molecular weight polyethylene (HMWPE) plasticized by wax. 采用石蜡增塑高相对分子质量PE后纺丝并经高倍拉伸制备高强高模纤维。
- A machine formerly used for spinning fibers such as cotton or wool. 废的旧纺机一种用于纺棉或毛纤的旧机器
- The research progress in the solution spinning and melt spinning of biodegradable poly(lactic acid) (PLA) fiber was reviewed and the fiber's properties as well. 综述了可生物降解聚乳酸纤维的溶液纺丝和熔融纺丝成形的研究进展,以及聚乳酸纤维的性能。
- melt spun fiber [化] 熔纺纤维
- The research progress in the solution spinning and melt spinning of biodegradable poly(lactic acid) (PLA) fiber was reviewed and the fibers properties as well. 综述了可生物降解聚乳酸纤维的溶液纺丝和熔融纺丝成形的研究进展，以及聚乳酸纤维的性能。
- Five technical processes of PET high|speed melt spinning, namely, MG, H4S, TCS, HCS and SHSS, were summarized. 综述了 PET高速纺丝热辊法生产工艺 (MG)、冷辊拉伸蒸汽定型法生产工艺 (H 4S)、热管法生产工艺 (TCS)、热管拉伸法生产工艺 (HCS)以及超高速纺丝工艺 (SHSS) ;
- The shaped silicon carbide fibers were prep ared from polycarbosilane by melt spinning,curing treatment and sinterin g. 以聚碳硅烷为原料,通过熔融纺丝、不熔化处理、烧成,制备出了具有异型截面的碳化硅纤维。
- Trilobal polycarbosilane(PCS) fibers were prepared by melt spinning PCS precursor through Y shaped spinnerret. 以聚碳硅烷(PCS)为原料,经不熔化和烧成制得三叶型碳化硅纤维。
- Trilobal polycarbosilane(PCS) fibers were prepared by melt spinning PCS precursor through Y-shaped spinnerret. 以聚碳硅烷（PCS）为原料，经不熔化和烧成制得三叶型碳化硅纤维。
- Trilobal polycarbosilane(PCS) fibers were prepared by melt spinning PCS precursor through Y shaped spinneret. 以聚碳硅烷(PCS)为原料,采用熔融纺丝制备三叶型PCS纤维后,经不熔化和烧成制得三叶型碳化硅纤维。
- The Sm(Co0.74CuxFe0.1Zr0.04)8(x=0,0.1, 0. 12,0. 16)ribbons with different Cu contents have been prepared by single roller melt spinning in Ar gas. 在氩气保护下用单辊熔体快淬法制备了不同Cu含量的Sm(Co0.;74CuxFe0
- The elastic recovery of melt-spun spandex can be improved by melt spinning self-made terminated polyurethane pre-polymer and spandex resin. 采用自制的封端型聚氨酯预取体与氨纶树脂熔融纺丝,可改善氨纶弹性恢复率。
- Carbon black was blended into thermoplastic polyurethane, the electrical conductive fiber was obtained by melting spinning. 摘要将导电炭黑混入到热塑性聚氨酯中，经熔融纺丝制得导电纤维。
- By trilobal spinning subassembly, the shaped polycarbosilane fibers were prepared from polycarbosilane by melt spinning. 以聚碳硅烷为原料，运用三叶型纺丝组件，通过熔融纺丝，制备出了异型截面聚碳硅烷纤维。
- The ribbon formation process and the technological parameters affecting the quality of melt spinning NiAl intermetallics were investigated. 摘要研究了金属间化合物快速凝固薄带的成型过程和影响薄带质量的工艺参数。
- We briefly describes the preparing and properties of the non- plasticate melt spinning PAN fibers as well as the resin that it made from. 综述了聚丙烯腈纤维的熔融纺丝工艺 ,主要介绍了非增塑融纺的聚丙烯腈树脂及纤维的制备方法和性质。