- The white corrosion products on hot dip Zn Al alloy coating exposed to seawater in dynamic aerated immersion were investigated by means of XRD and TEM. 采用XRD和TEM对热浸锌铝合金镀层在动态充气海水全浸试验时所形成的白色腐蚀产物进行了研究。
- The hot dip Zn Ni alloy coating provides good anticorrosion performance. Two kinds of materials, Q235 and Q345 used for galvanizing Zn and Zn Ni alloy. 对Q2 35和Q345两种材料表面热浸镀纯Zn和Zn Ni合金 ,研究Ni对热镀锌耐蚀性的影响。
- In this paper, the adhesiveness and the corrosion resistance of hot dip Zn 0.1Ni alloy coating are studied by the bending test and the salt spray test and are compared with those of hot dip zinc coating. 通过弯曲试验和盐雾试验,研究了热浸Zn?0.;1Ni合金镀层的粘附性能和耐腐蚀性能,并与热浸锌镀层对比。
- A hot dip Zn 5%Al RE coating on high carbon steel wire is tested. 试验了在高碳钢丝表面上热浸镀Zn 5%25Al RE合金层。
- hot dip Zn - 5% Al-mischmetal alloy coated wires 热镀锌-5%25铝稀土合金
- The tensile properties and corrosion resistance of hot dip 55%Al Zn alloy coating steel are investigated. 研究了热浸镀 5 5%25Al Zn合金镀层钢的室温拉伸性能和耐蚀性能。
- STUDY ON ADHESIVENESS AND CORROSION RESISTANCE OF HOT DIP Zn 0.1Ni ALLOY COATING 热浸 Zn-0.;1Ni 合金镀层粘附性和耐腐蚀性研究
- Keywords hot dip Zn Ni alloy coating;hot dip galvanizing;adhesiveness;corrosion resistance; 热浸锌镍合金镀层;热镀锌;粘附性;耐腐蚀性;
- The results show that the room temperature yield strength and tensile strength of hot dip 55%Al Zn alloy coating steel are higher than those of low carbon steel (Q235) plates, and its elongation has not reduced. 结果表明 :Q2 35钢板经热浸镀 5 5%25Al Zn合金后的室温屈服强度和抗拉强度均高于Q2 35钢 ,而伸长率没有降低。
- hot dip Zn Ni alloy coating 热浸锌镍合金镀层
- The strengthening mechanism of Zn Al Cu pseudo alloy coating and relationship among hardness,aging temperature and time are studied by SEM,XRD,EDX and hardness test. 利用扫描电镜(SEM )、X射线衍射分析 (XRD)、能谱分析 (EDX)和硬度测试等手段 ,对涂层的性能进行了测试 ,分析研究了Zn Al Cu伪合金涂层硬度与时效温度和时效时间的关系 ,并探讨了强化机理。
- The technique of hot dip Zn-Ni alloy coating is an effective method for solving the reactive steel problem in hot dip galvanizing. 热浸锌镍合金镀层技术是解决活性钢热镀锌问题的有效方法。
- For acquiring new alloy coating with good corrosion resistance and production cost equivalence with hot dip zinc coating,the hot-dip Zn-Mg alloy coating of containing 0. 质量分数,下同)的热镀锌镁合金镀层,对各种成分的锌镁合金镀层进行了电化学测试和中性盐雾实验,并通过电子扫描显微镜观察了镀层的表面形貌。
- The surface morphology and composition of Zn 5%Al RE coating hot dip plated on alloy steel wire was analyzed by means of metallography,SEM and EPMA. 本文采用金相显微镜、扫描电镜和能谱仪等设备分析了在Zn?5%25 Al?RE合金溶液中热浸镀中碳钢丝表面的组织形貌和成分。
- The friction and wear properties of 2 kinds of high strength Zn Al alloys and 3 kinds of Cu alloys are demonstrated. Under different lood and rotative velocity, the friction factor and abrasion wear of the alloys and their coupling samples are given. 采用MM200磨损试验机,测定和对比了铸造锌铝合金(ZZnAl27Cu2A和ZZnAl27Cu2D)和工业上常用铜合金(ZCuSn6Zn6Pb3,ZCuA110Fe3和ZCuZn33Mn2Pb2)的摩擦磨损特性。
- Seawater corrosion behavior of hot dip galvanized steel wires,a long with0.2%Al-Zn-RE,5%Al-Zn-RE and55%l-Zn-Si alloy coated steel wires,are in vestigated in comparison. 以热浸镀Zn、0.;2%25Al-Zn-RE、5%25Al-Zn-RE和55%25Al-Zn-Si合金镀层钢丝为研究对象;进行了为期6个月的室内海水浸泡试验。
- The recommended passivating solution could be used not only for passivating zinc hot dipped coating but also for Zn-Ni and Zn-Fe alloy coating. 结果表明,该钝化液适合于热浸锌合金镀层的表面钝化处理,亦适用于电镀锌及锌合金镀层、锌合金压铸件等的钝化处理,应用范围宽,且工序简化,抛光和钝化一步完成。
- Keywords Zn Al alloy;super plasticity;phase boundary sliding(PBS); 锌铝合金;超塑性;相界滑移;
- A Study on the Effects of RE on Hot Dip Al-3Si Alloy Coating 稀土对热浸Al-3Si合金镀层影响的研究
- Keywords Zn Al Alloy;Bottom Shrinkage;Composition Undercooling;Gravity Segregation; 锌铝系合金;底缩;成分过冷;重力偏析;