- With carbon steel pretreated with flux, hot dip coating process and bimetal producing of ZAS35 alloy/carbon steel as well as bimetal interface characteristic were studied. 研究了经熔剂法预处理的碳钢热浸镀ZAS35锌合金工艺、ZAS35锌合金 /碳钢双金属制作工艺及双金属界面特性。
- [Abstract] With carbon steel pretreated with flux, hot dip coating process and bimetal producing of ZAS35 alloy/carbon steel as well as bimetal interface characteristic were studied. [摘 要] 研究了经熔剂法预处理的碳钢热浸镀ZAS35锌合金工艺、ZAS35锌合金/碳钢双金属制作工艺及双金属界面特性。
- TiO_2 nano thin film was prepared on ITO glass substrate by dip coating and spin coating process. 以TiCl_4和C_(16)H_(36)O_4Ti溶胶为前驱体,分别采用旋转-涂覆法和浸渍-提拉法制备了纳米TiO_2薄膜。
- The research in flux is mainly to change the original double hot dip coating technique, and change the first hot-dip galvanizing into electrolyzing flux. 对于助镀剂的研究主要是改变原有的双热浸镀工艺，改第一次热浸镀锌为电解助镀。
- The TiO_2 nano thin film prepared by spin coating process is white, while the TiO_2 nano thin film made by dip coating process is colorless and transparent. 以TICl_4为通过旋转.;涂覆法制备的纳米TiO_2薄膜;表观为白色不透明膜;而以C_(16)H_(36)O_4Ti为前驱体选用浸渍-提拉法制备的薄膜为无色透明膜。
- The passivating process and formulation of bath solution for zinc hot dipped coating with higher alloy content were investigated and discussed. 研究了合金含量较高的热浸镀锌层的钝化工艺及配方，探讨了钝化液组分对钝化膜性能的影响及钝化原理，检测了所研制钝化膜的性能。
- Corrosion Mechanism of 55 Al-Zn Hot Dip Coating 55Al-Zn合金镀层耐蚀机理的研究
- Hot Dip Coating of 55Al-Zn for NdFeB Magnets 烧结NdFeB磁体热浸镀55Al-Zn合金研究
- The recommended passivating solution could be used not only for passivating zinc hot dipped coating but also for Zn-Ni and Zn-Fe alloy coating. 结果表明，该钝化液适合于热浸锌合金镀层的表面钝化处理，亦适用于电镀锌及锌合金镀层、锌合金压铸件等的钝化处理，应用范围宽，且工序简化，抛光和钝化一步完成。
- Influence of Rare Earth Element during Hot Dip Coating 稀土元素在热浸镀中的作用
- A hot dip Zn 5%Al RE coating on high carbon steel wire is tested. 试验了在高碳钢丝表面上热浸镀Zn 5%25Al RE合金层。
- Immersion Corrosion Behavior of Hot Dip Coated Zn- Al Coating in Seawater 热浸镀层的海水全浸腐蚀行为研究
- Immersion Corrosion Behavior of Hot Dip Coated Zn-Al Coating in seawater 热浸镀层的海水全浸腐蚀行为研究
- The Microstructure of Zn-5%Al Hot Dip Coating and Study on Its Corrosion Resistant Mechanism Zn-5%25Al合金热浸镀层微结构及其防腐机理研究
- powder dip coating process [化] 粉末浸涂法
- dip coating process [化] 浸涂法
- Simulated Sea Water Corrosion of Aluminmn Hot Dipped Coating 热浸镀铝层耐人造海水腐蚀性的电化学研究
- Compile and develop SSEAC/ STS assembly/ coating process. 制订和完善SSEAC/TS总装/塑生产工艺流程。
- The Annealing Furnace is a key Equipment for any Hot Dip Galvanizing Line. 对于任何连续热镀锌线退火炉都是关键设备。
- Pure and Pt doped ( m( Pt ):m( WO 3)=0.3%) WO 3 thin films were prepared using the sol gel process by the dip coating technique on alumina substrates. 用溶胶凝胶浸渍技术在三氧化二铝基片上制备了纯和 (m(Pt) :m(WO3 ) =0 .;3%25 )铂搀杂的三氧化钨膜