- Shrinkage stress was found to increase linearly with cure temperature. 我们发现收缩应力随固化温度直线增加。
- The above times do not include the time for the workpiece to reach the curing temperature. 上述时间不包括工件加热所需时间。
- As for curing process,the influence of dosage of curing agent and curing temperature on gel time was investigated. 在固化工艺方面,研究了固化剂含量和固化温度对于凝胶时间的影响。
- The influences of shear ratio,curing temperature and processing technology on the properties of TPE were explored. 实验结果表明:密炼机制备的TPE的力学性能明显优于双辊开炼机,且密炼机的剪切速率越高,TPE的性能越好;
- Rate of Cure and Final Strength will Depend on the Resistance time at the Cure Temperature. 固化比率及最终固化强度取决于在固化温度条件下所持续的固化时间。
- When curing temperature below glassy temperature of adhesive coating, bonding strength is reduce with curing extent increase. 固化温度低于胶层的玻璃化温度时，粘接强度随着固化程度的提高而降低。
- The paper also studies the effects of some factors such, as additives contont, curing temperature,adherend and storage life on the adhesive property. 文中还对效果较好的体系,进行了添加量、固化温度、被粘材料以及存放时间等因素对粘接性影响的探索。
- By property modification,the phenolic resin will perform special abilities in hydration resistance,oxidation resistance and higher curing temperature. 通过对酚醛树脂的改性,使其具有抗水化性、抗氧化性和高固化温度等特殊性能;
- The researches indicated that the self-made curing agent could decrease the volatile matter of phenolic resin,curing temperature sharply,impro... 该胶黏剂作为中温固化耐高温灌封胶黏剂可以满足航空工业耐高温的技术要求。
- The surface modification of MWNT decreased the curing temperature of the system and improved the adhesion between MWNT,benzoxazine and epoxy. 对MWNT进行了表面改性,降低了苯并恶嗪和环氧树脂固化的温度,增强了MWNT与苯并恶嗪/环氧树脂基体间的结合力。
- The research result shows that resorcinol has obvious effect on decreasing curing temperature and increasing curing rate of PF resin in certain scope. 研究结果表明,间苯二酚在一定范围内对降PF树脂的固化温度、提高固化速度具有明显的作用。
- It is found by comparing trial results that curing temperature has influence on strength and shrinkage performance of cement-stabilized macadam. 比较这2种养生温度下的试验结果发现：养生温度对水泥稳定碎石的强度及收缩性能均有影响；
- The surface modification of MWNT decreased the curing temperature of the system and improved the adhesion between MWNT, benzoxazine and epoxy. 对MWNT进行了表面改性，降低了苯并恶嗪和环氧树脂固化的温度，增强了MWNT与苯并恶嗪/环氧树脂基体间的结合力。
- The effects of types and doses of intensifier,curing temperature,and curing time on intensity of the consolidating body were investigated. 为将声波速度应用于注浆质量检测中 ,就声波速度与注浆固结体单轴抗压强度之间的关系进行了研究。
- Effects of graphite content,curing time and curing temperature on the properties of the composite were studied with orthogonal test. 采用正交试验方法研究了石墨含量、固化时间以及固化温度对复合材料的影响。
- As the amount of curing agent and the curing temperature is raised,the curing time is shortened and the curing result is improved. 实验结果表明其固化时间均随固化剂用量的增加和固化温度的升高而缩短,且固化产物性能提高。
- The kind of pps Can be used as heat-stable and Corrosion-resistant Coating material With much lower Curing temperature than that needed by the Ryton V-1 PPS resin. 此类聚苯硫醚树脂可用作耐热、防腐涂层材料。 固化温度较Ryton V_1型树脂低.
- Epoxy resin, magnetic forro oxide and curring agent were used to synthetis feroxide magnetic primer.It has the features of harmless,lower curing temperature. 选用环氧树脂、磁性氧化铁和固化剂合成磁性氧化铁环氧漆，具有无毒、低温固化、性能好等特点。
- In this article,we studied the effect of bisphenol AF、BPP on the vulcanization property of fluororuber and studied the effect of curing temperature on the Vulcanization property. 研究了双酚AF硫化体系中硫化剂双酚AF、促进剂BPP对氟橡胶硫化特性的影响以及硫化温度对硫化特性的影响。
- With the increasing of cure temperature, the scorch time and optimum cure time decreased, but the crosslink density had a tread of decreasing. 硫化温度的提高会缩短焦烧时间和正硫化时间,但有使交联密度下降的趋势。