- 加入少量Sr可使鎂合金AZ91D-0.3%Be-Sr的組織得到細化,力學性能顯著提高。Small amount of Sr addition can refine as-cast microstructure of AZ91D-0.3%25Be alloy and efficiently improve mechanical properties of AZ91D-0.3%25Be alloy.
- 鎂合金AZ91DAZ91D Magnesium alloy
- 研究了鎂合金AZ91D-0.3%Be-Sr的阻燃性及Sr對合金顯微組織和力學性能的影響,結果表明,在鎂合金AZ91D中加入0.3%Be,顯著提高了阻燃性,使試驗合金可在無覆蓋和保護的條件下直接暴露在大氣中熔煉。Ignition-proof property of AZ91D-0.3%25Be-Sr magnesium alloy and influence of Sr addition on microstructure and mechanical properties of AZ91D-0.3%25Be alloy were investigated. The results show that 0.3%25 Be addition to AZ91D magnesium alloy can effectively increase its ignition-proof property, and the experimental alloy can be melted in air.
- 機械力表面改性對鎂合金含鋁塗層耐腐蝕性能影響的研究Influence of surface modification by mechanical force on corrosion resistance of aluminium-containing coatings on Mg alloys
- 硫酸鎂bitter salt
- TiC/AZ91DTiC/AZ91D
- 電參數對鎂合金微弧氧化陶瓷層緻密性和電化學阻抗的影響Effects of Electric Parameters on Density and Electrochemical Impedance of Ceramic Layer Made by Micro-arc Oxidization on Magnesium Alloy
- 鎂合金magnesium alloy
- 鎂鋁magnalium
- Al2O3-SiO2/AZ91D鎂基複合材料Al2O3-SiO2/AZ91D magnesium matrix composites
- 真空低壓鎂合金消失模鑄造生產線的三維設計及自動控制3D Design and Automation of Vacuum and Low Pressure-Expendable Pattern Casting Process Product Line
- 熱處理后(T4和T6),由於AZ91D具有固溶強化和時效強化效果, 合金的性能相對於壓鑄態有大幅度的提高。Mechanical properties after T4 and T6 tempering got marked improvement as AZ91D can be solution and aging strengthened while vacuum assisted die casting gave it this opportunity.
- ZA84鎂合金ZA84 magnesium alloy
- EM21鎂合金ZM21 magnesium alloy
- 通過添加鈹和稀土,得到了著火點溫度提高約250℃、可直接暴露在大氣中熔煉的鎂合金,其力學性能與AZ91D接近。Abstract By the addition of Be and RE,the ignition temperature of ignitionproof magnesium alloy was raised 250 higher than that of AZ91D,it can be melted in air and its mechanic properties approach that of AZ91D.
- AZ91D鎂合金AZ91D magnesium alloy
- AZ31B鎂合金AZ31B magnesium alloy
- 釔鎂合金Y-Mg alloy
- 鋅鎂合金Zn Mg Alloy
- AZ80鎂合金AZ80 magnesium alloy