- The equivalent circuit models corresponding to these anodic alumina membranes were established. 结果表明:在草酸、磷酸电解液中形成的阳极氧化铝膜是多孔双层膜。
- Nano-Cu/Al 2O 3 assemblies were prepared by AC electrochemical deposition of Cu in the ordered pores of alumina membranes. 以有序的多孔氧化铝为模板 ;利用交流电在孔洞中沉积金属铜得到纳米Cu粒子 Al2 O3 组装体系 .
- The result shows that the anodic alumina membranes produced in oxalic acid or phosphoric acid electrolyte are porous double-layer films. 在硫酸电解液中形成的直流阳极氧化铝膜的等效电路中无多孔层信息。
- Abstracts Recently, alumina membranes have attracted enormous interest.Anodic Aluminum Oxide (AAO) is a kind of transparent template with high-ordered nano-pores. 摘 要 近年来研究制备具有纳米结构的氧化铝多孔膜越来越受到人们的关注。
- Anodization of high purity Al foil in phosphoric acid solution at different pressures was experimentally studied to understand the formation mechanism of the nano-porous anodic alumina membranes. 摘要为探讨多孔铝阳极氧化膜的形成机理，研究了不同气压条件下铝在磷酸溶液中的阳极氧化过程，发现在真空下进行阳极氧化，氧气析出非常明显。
- The barrier-layer alumina films and porous-layer alumina make up of nanometer alumina membrane. 其中阻挡层氧化铝和多孔层氧化铝构成纳米氧化铝模板。
- Porous alumina membrane is prepared by aluminum anodizing in given acidic solution. 直流恒压下,在酸性溶液中对铝实施两步阳极氧化制备了多孔氧化铝膜。
- In this paper porous alumina membrane is used as template to synthesize Ni nanoarray and electrical deposition is applied. 本文以纳米孔的多孔氧化铝膜作为模板，采用电化学沉积法在孔内合成出高度有序的镍纳米阵列体系。
- Highly ordered iron oxide nanowire arrays were prepared by sol-gel tem plate method within the pores of anodic alumina membrane (AAM). 氧化铁纳米线阵列的制备未见报导,因此氧化铁纳米线阵列的制备及其性质的研究具有重要的意义。
- We report the numerical calculation results of ordered silver nanowire arrays embedded in anodic alumina membrane (AAM). 摘要报道了组装在氧化铝模板中的银纳米线有序阵列光偏振的数值计算结果。
- A metallographic microscope is used to observe the micrographs of the porous alumina membrane anodized by first and second steps. 用金相显微镜观察了一次阳极氧化和二次阳极氧化后多孔氧化铝的表面形貌。
- Alumina membrane with nano-porous was prepared through a single-step anodization procedure.Superhydrophobic surfaces were achieved after the treatment of membrace by fluoroalkyl. 通过简单的电化学阳极氧化的方法制备氧化铝膜,氟硅烷修饰后获得超疏水表面。
- The effect of viscosity and dipping time on membrane, and that of calcining temperature and time on the structural properties of alumina membrane are also discussed. 还研究了膜厚与浸渍时间和粘度等的关系以及对比不同焙烧温度和时间对氧化铝膜的结构影响。
- The method of producing anodic alumina membrane is presented.The route to synthesize nanowires through electrodeposition with it as a membrane is reviewed. 本文论述了阳极氧化铝模板的制备方法和以其为模板利用电沉积技术制备纳米线的合成路线。
- The art preparation of alumina membrane with sol-gel has been studied, in which acids have been used as peptizers.Concentration and peptization temperature of acids have been determined. 研究了溶胶-凝胶法制备氧化铝无机膜的工艺过程，确定了作为胶溶剂的酸及其用量以及胶溶温度；
- Template Synthesis of Nanostructure Materials in Anodic Alumina Membranes 多孔铝模板合成纳米材料的研究
- Keywords porous anodic alumina membranes;anodic oxidization;nanostructure; 多孔氧化铝模板;阳极氧化法;纳米结构;
- ultrafiltration alumina membrane γ-Al2O3超滤膜
- Annealing Effect on Photoluminescence of Alumina Membranes with Ordered Pore Arrays 退火对有序孔洞氧化铝膜荧光性能的影响