- Besides, the silicone monomer and the acrylate monomer were also introduced. 同时,对有机硅单体和丙烯酸酯单体也作了介绍。
- That is: acrylate monomer 100g, DVB 1.8g, BPO Ig, DMA 0.2g, SiO2 0.18g, the reaction condition is 27t:/10h, the post-treatment processing is 160t:/6h. 通过一系列的试验,最后得到较优化的配方及工艺:丙烯酸酯单体100g,二乙烯基苯1.;8g,过氧化苯甲酰1g,N,N-二甲基苯胺0
- Acrylate monomer with polyoxyethylene group chain and a series of polycarboxylic superplasticizer were synthesized and their water-reducing effects were investigated. 介绍了聚氧乙烯基烯丙酯大单体和聚羧酸减水剂的合成,并对合成的聚羧酸减水剂进行了性能考察。
- Self-preparation polymerizable macromolecular surfactant HTP and acrylate monomer were used to prepare the amphiphilic polymer by soap-free microemulsion pentamer copolymerization. 以自制可聚合大分子表面活性剂HTP与丙烯酸酯类单体进行无皂微乳液五元共聚,制备可热固化双亲聚合物。
- The effects of the content of BPO, acrylate monomer, AA and emulsifier on viscosity and T style peel strength of SBS emulsion adhesive modified by acrylate were discussed in this paper. 讨论了BPO的用量、丙烯酸酯单体的用量、功能单体AA的用量以及乳化剂的用量对丙烯酸酯改性SBS乳液型胶粘剂粘度和T剥离强度的影响。
- The DMBA acrylate resin was prepared by the copolymerization of the functional monomer with acrylate monomers, and the anti-fouling activity of the resin was studied. 将该单体与丙烯酸酯类单体共聚制备了DMBA丙烯酸树脂,初步研究了树脂的防污性能。
- Water-borne acrylic resin was modified by grafted copolymerization of acrylic monomer and epoxy resin. 通过丙烯酸酯类单体与环氧树脂接枝共聚反应,对水性丙烯酸树脂进行改性。
- By the high-energy radial, acrylic monomer is grafted on the surface of polypropylene filler. 应用高能射线辐照技术,在聚丙烯填料表面接枝丙烯酸单体进行改性。
- A newly developed grafting copolymer of synthetic rubber with acrylic monomer has been reported. 报道了将丙烯酸单体接枝到合成橡胶上的接枝共聚方法。
- Acrylate monomers were grafted at the outfield of butadiene-styrene polymer by polymerizing in emulsion. 通过乳液聚合的方法,在丁苯乳液粒子的外层接上丙烯酸酯单体。
- The results show that polysiloxane is effectively copolymerized with acrylate monomers. 研究结果表明,聚硅氧烷被有效地共聚到丙烯酸酯单体中。
- The preparation process and the related properties of the cold-seal adhesive polymerized from acrylate monomers were included in the paper. 本研究采用丙烯酸酯单体聚合制成一种全新的合成冷封胶。介绍了制备方法和有关性能。
- The emulsion with core-shell structure was prepared with organosilicon and acrylate monomers through emulsion polymerization. 摘要用有机硅及丙烯酸酯单体通过乳液聚合制备了具有核壳结构的共聚物乳液。
- An aqueous polyurethane-polyacrylate hybrid emulsion was prepared by soap-free emulsion polymerization of aqueous polyurethane emulsion with C C double bond modified with acrylic monomer through grafting copolymerization. 采用无皂乳液聚合方法,用丙烯酸酯单体对含C C双键的水性聚氨酯进行接枝共聚改性,制得丙烯酸酯改性聚氨酯无皂乳液。
- The emulsion polymerization was used to copolymerize the hexafluorobutyl acrylate monomer, and other acrylic monomers in order to obtain a stable emulsion. 摘要采用乳液聚合的方法,将丙烯酸六氟丁酯单体和其他的丙烯酸酯单体进行了共聚,得到了稳定的乳液。
- The thermal stabilities and the decomposition kinetics of the copolymers of t?butyl?3?isopropenylcumylperoxide (D120) with styrene and/or methyl acrylate monomers were studied using differential scanning calorimetry. 用示差扫描量热法研究了1-(2-叔丁基过氧异丙基)-3-异丙烯基苯与苯乙烯、丙烯酸甲酯单体共聚后所得大分子过氧化物的热稳定性以及分解动力学。
- Keywords microwave;valonea extract;acrylate monomer;graft modification; 微波;橡椀栲胶;丙烯酸(酯);接枝改性;
- The stable fluorine-contained acrylic ester copolymer emulsion (FPA-R) was prepared by FMA and acrylate monomers. 以甲基丙烯酸十二氟庚酯(FMA)与丙烯酸酯类单体,成功合成了稳定性好的含氟丙烯酸酯聚合物FPA-R乳液。
- The experimental result indicated that the nitrocellulose emulsion modified by acrylic monomer monomers was better than that of alkyd. 结果表明,丙烯酸酯类单体改性互穿聚合物网络聚合法制得的乳液效果好。
- Monocomponent acrylic cathodic electrophoretic coating was prepared by copolymerization of blocked unsaturated isocyanate and acrylate monomers. 在此采用封闭不饱和异氰酸酯与常用的丙烯酸酯类单体共聚制备单组分丙烯酸阴极电泳涂料。