The results showed that the higher internal stress and serious carbide network in the banded carbide in the inner roll body were the main causes of heavy back-up roll stationary cracking.

• 结果表明,辊身心部较高的内应力和在带状碳化物中存在严重的网状碳化物是造成大型支承辊置裂的主要原因。