The results show that both the slow cooling rate to control ferrite transformation and the rapid cooling rate to control bainite transformation affect the microstructure of TRIP steel obviously.

• 结果表明，热变形后控制铁素体相变的慢速冷却的速度及控制贝氏体相变的快速冷却的速度对最终组织的组成影响较大；