The result showed that the shrinkage cavity formed during foundry and the disfigurement of graphite were the main cause of the driving wheel cracking.

• 结果表明,产生裂纹的主要原因是驱动轮在铸造中形成的缩松孔隙和石墨形态缺陷所致。