The intergranular-type structure induced the transgranular fracture during loading,and the material was enhanced but fracture strength was poor due to grain-boundary sliding.

• 当受到外力时既能诱发穿晶断裂，又能引起裂纹偏转，起增强作用，但由于产生晶界滑移，材料韧性有所下降。