Plenty of oxidation etching pits are found on the surface of the specimen after the thermal fatigue test,and the surface principal crack is prone to propagate through these etching pits.

• 实验结果发现,试样表面出现大量的氧化腐蚀坑,表面主裂纹优先通过这些腐蚀坑扩展。