Many leakages at welds of the old tube system were found in gastight test, and the cause was verified by site investigation to be welding cracks produced in original manufacture and construction.

• 分别对焊缝区裂纹和母材热影响区裂纹的形态和产生原因进行分析,指出此裂纹属沿晶开裂,由组织粗大和焊接热应力引起,并根据分析的原因制订了缺陷的修复方案和具体的修复措施,缺陷修复后经气密检验合格。