It is found that graphitization induced instability of the crystal lattice is the main reason for laser induced damage.

• 分析了不同激光工作参数对金刚石薄膜的激光损伤机理,认为石墨化导致晶格失稳是金刚石薄膜激光损伤的主要原因。