It has been proved that these cracks are caused by sulfide stress corrosion cracking(SSCC) through fail ure analysis and service environment survey.

• 通过失效分析和管道服役环境调查，证明开裂原因是管道服役期间发生硫化物应力腐蚀开裂（SSCC）。