- The hot dip Zn Ni alloy coating provides good anticorrosion performance. Two kinds of materials, Q235 and Q345 used for galvanizing Zn and Zn Ni alloy. 对Q2 35和Q345两种材料表面热浸镀纯Zn和Zn Ni合金 ,研究Ni对热镀锌耐蚀性的影响。
- Keywords hot dip Zn Ni alloy coating;hot dip galvanizing;adhesiveness;corrosion resistance; 热浸锌镍合金镀层;热镀锌;粘附性;耐腐蚀性;
- hot dip Zn Ni alloy coating 热浸锌镍合金镀层
- The white corrosion products on hot dip Zn Al alloy coating exposed to seawater in dynamic aerated immersion were investigated by means of XRD and TEM. 采用XRD和TEM对热浸锌铝合金镀层在动态充气海水全浸试验时所形成的白色腐蚀产物进行了研究。
- A hot dip Zn 5%Al RE coating on high carbon steel wire is tested. 试验了在高碳钢丝表面上热浸镀Zn 5%25Al RE合金层。
- In this paper, the adhesiveness and the corrosion resistance of hot dip Zn 0.1Ni alloy coating are studied by the bending test and the salt spray test and are compared with those of hot dip zinc coating. 通过弯曲试验和盐雾试验，研究了热浸Zn?0.;1Ni合金镀层的粘附性能和耐腐蚀性能，并与热浸锌镀层对比。
- hot dip Zn - 5% Al-mischmetal alloy coated wires 热镀锌-5%25铝稀土合金
- Process for Black Chromating of Zn Ni Alloy Coating 锌镍合金镀层的黑色钝化
- STUDY ON ADHESIVENESS AND CORROSION RESISTANCE OF HOT DIP Zn 0.1Ni ALLOY COATING 热浸 Zn-0.;1Ni 合金镀层粘附性和耐腐蚀性研究
- The effect of Ni content in Zn bath on thickness of hot dip galvanized coating was studied using SEM. 应用SEM、EPMA等方法研究了锌浴中镍含量对热浸锌镀层厚度的影响，试验结果表明：当锌浴中镍含量小于0.;12%25 (wt)时，镀层随镍含量增加而减薄；
- The tensile properties and corrosion resistance of hot dip 55%Al Zn alloy coating steel are investigated. 研究了热浸镀 5 5%25Al Zn合金镀层钢的室温拉伸性能和耐蚀性能。
- The surface morphology and composition of Zn 5%Al RE coating hot dip plated on alloy steel wire was analyzed by means of metallography,SEM and EPMA. 本文采用金相显微镜、扫描电镜和能谱仪等设备分析了在Zn?5%25 Al?RE合金溶液中热浸镀中碳钢丝表面的组织形貌和成分。
- The results show that the room temperature yield strength and tensile strength of hot dip 55%Al Zn alloy coating steel are higher than those of low carbon steel (Q235) plates, and its elongation has not reduced. 结果表明 :Q2 35钢板经热浸镀 5 5%25Al Zn合金后的室温屈服强度和抗拉强度均高于Q2 35钢 ,而伸长率没有降低。
- Surface quality of hot dip plating Zn-Al alloy were further improved. 采用该合金助镀剂进行Zn Al合金热浸镀的样品 ,表面质量得到进一步改善。
- The technique of hot dip Zn-Ni alloy coating is an effective method for solving the reactive steel problem in hot dip galvanizing. 热浸锌镍合金镀层技术是解决活性钢热镀锌问题的有效方法。
- Effects of cooling rate on eutectic microstructure of Zn-(0.24Ni) alloy for hot dip galvanization were investigated. 研究了冷却速度对用于热浸镀Zn的Zn0.;24Ni合金共晶组织的影响。
- In order to clear the phenomenon,the Al-Fe alloy liquids used in hot dip aluminizing were quickly solidified and slowly solidified respectively. 分别将热浸镀含稀土和不含稀土的铝液体急冷和缓冷后分析表明,镀铝后的铝-铁合金液在急冷过程中具有非晶形成能力;
- The kinetics curves of alloy layer growth in hot dip aluminizing layer and corresponding equations were given with computer fitting. 根据试验结果,通过计算机拟合给出了合金层生长动力学曲线,并建立了方程。
- Seawater corrosion behavior of hot dip galvanized steel wires,a long with0.2%Al-Zn-RE,5%Al-Zn-RE and55%l-Zn-Si alloy coated steel wires,are in vestigated in comparison. 以热浸镀Zn、0.;2%25Al-Zn-RE、5%25Al-Zn-RE和55%25Al-Zn-Si合金镀层钢丝为研究对象;进行了为期6个月的室内海水浸泡试验。
- Knitting used Tinned Plated CCS Wire is made by washing over with a coating of tin or tin-lead alloy on the surface of copper coated wire by hot dip method. 编织镀锡铜包钢细线 是在铜包线表面用热镀的方法镀上一层均匀的锡或锡铅合金。