- The tensile properties and corrosion resistance of hot dip 55%Al Zn alloy coating steel are investigated. 研究了热浸镀 5 5%25Al Zn合金镀层钢的室温拉伸性能和耐蚀性能。
- The results show that the room temperature yield strength and tensile strength of hot dip 55%Al Zn alloy coating steel are higher than those of low carbon steel (Q235) plates, and its elongation has not reduced. 结果表明 :Q2 35钢板经热浸镀 5 5%25Al Zn合金后的室温屈服强度和抗拉强度均高于Q2 35钢 ,而伸长率没有降低。
- A hot dip Zn 5%Al RE coating on high carbon steel wire is tested. 试验了在高碳钢丝表面上热浸镀Zn 5%25Al RE合金层。
- The surface morphology and composition of Zn 5%Al RE coating hot dip plated on alloy steel wire was analyzed by means of metallography,SEM and EPMA. 本文采用金相显微镜、扫描电镜和能谱仪等设备分析了在Zn?5%25 Al?RE合金溶液中热浸镀中碳钢丝表面的组织形貌和成分。
- EFFECT OF Si ON THE INTERFACIAL BONDING STRENGTH OF Al- Pb ALL OY STRIPSAND HOT DIP AL UMINIZED STEEL SHEETSBY HOT ROL LING 硅对铝铅轴承合金带与热浸铝钢板热轧复合界面强度的影响
- The white corrosion products on hot dip Zn Al alloy coating exposed to seawater in dynamic aerated immersion were investigated by means of XRD and TEM. 采用XRD和TEM对热浸锌铝合金镀层在动态充气海水全浸试验时所形成的白色腐蚀产物进行了研究。
- The effect of Ni content in Zn bath on thickness of hot dip galvanized coating was studied using SEM. 应用SEM、EPMA等方法研究了锌浴中镍含量对热浸锌镀层厚度的影响,试验结果表明:当锌浴中镍含量小于0.;12%25 (wt)时,镀层随镍含量增加而减薄;
- The hot dip Zn Ni alloy coating provides good anticorrosion performance. Two kinds of materials, Q235 and Q345 used for galvanizing Zn and Zn Ni alloy. 对Q2 35和Q345两种材料表面热浸镀纯Zn和Zn Ni合金 ,研究Ni对热镀锌耐蚀性的影响。
- Commodity:Hot dipped galvanized steel in coil . 货物名称:冷轧热镀锌卷。
- The technique of hot dip Zn-Ni alloy coating is an effective method for solving the reactive steel problem in hot dip galvanizing. 热浸锌镍合金镀层技术是解决活性钢热镀锌问题的有效方法。
- In this paper, the adhesiveness and the corrosion resistance of hot dip Zn 0.1Ni alloy coating are studied by the bending test and the salt spray test and are compared with those of hot dip zinc coating. 通过弯曲试验和盐雾试验,研究了热浸Zn?0.;1Ni合金镀层的粘附性能和耐腐蚀性能,并与热浸锌镀层对比。
- Bitumen coated and Hot Dip Galv. steel fence post. the length range from 450mm to 2400mm.... 发布者:马传圆所在地:新疆吐鲁番地区行业:五金、工具职位:外销员工作年限:在读学生
- Compared with spot welding of low carbon cold rolled steel,weldability of hot dip galvanized steel sheet worsened. 热镀锌钢板与普通低碳冷轧钢板相比,其点焊焊接性能显著恶化。
- The development, prpcess, principle and characteristics of hot dip aluminizing technique are reviewed, and the microstructure and formation mechanism of Fe - Al intermetallics are analyzed. 综述了热浸镀铝钢镀铝层的组织、形成机理、生长动力学和扩散后组织的研究现状,指出了热浸镀铝钢今后的研究方向。
- The Annealing Furnace is a key Equipment for any Hot Dip Galvanizing Line. 对于任何连续热镀锌线退火炉都是关键设备。
- In order to improve the property of 1Cr18N9Ti and 1Cr13 stainless steel used at high temperature, tests of hot dip aluminizing and oxidation resistance were done on them. 为进一步提高 1Cr18Ni9Ti、1Cr13不锈钢的高温使用性能 ,本文对两种材料进行了热浸镀稀土铝合金处理和抗高温氧化性能的试验。
- Seawater corrosion behavior of hot dip galvanized steel wires,a long with0.2%Al-Zn-RE,5%Al-Zn-RE and55%l-Zn-Si alloy coated steel wires,are in vestigated in comparison. 以热浸镀Zn、0.;2%25Al-Zn-RE、5%25Al-Zn-RE和55%25Al-Zn-Si合金镀层钢丝为研究对象;进行了为期6个月的室内海水浸泡试验。
- High structure strengh,hot dip galvanized,greatly protract time of use. 高强度管材、产品经热镀锌处理、大大地延长了使用寿命;
- Surface quality of hot dip plating Zn-Al alloy were further improved. 采用该合金助镀剂进行Zn Al合金热浸镀的样品 ,表面质量得到进一步改善。
- With carbon steel pretreated with flux, hot dip coating process and bimetal producing of ZAS35 alloy/carbon steel as well as bimetal interface characteristic were studied. 研究了经熔剂法预处理的碳钢热浸镀ZAS35锌合金工艺、ZAS35锌合金 /碳钢双金属制作工艺及双金属界面特性。